Tecnate TMN 2535 is a MDI-PTMEG prepolymer. This High Performance hot cast; when cured with 1; 4 BDO; yields a 90 Shore A hardness. Technate TMN 2535 can be used in various industries such as: wheels; rollers; bushings; pipelining; and belts.
File Downloads
Technical Data SheetApplications
- Belts
- Bushings
- Fork Lift Tires
- Mining
- Pipelining
- Wheels
Advantages
- Abrasion resistance
- Excellent Rebound
- Hydrolytic stability
Product Types
Prepolymer
Product Testing
| Test Performed | Test Results |
| Color - ISO | Hazy Viscous liquid |
| Compressive Strength - ASTM D695 - @ 10% Strain | 18 psi |
| Compressive Strength - ASTM D695 - @ 20% Strain | 349 psi |
| Demold Time | 1 Hours |
| Elongation - ASTM D412 - Cured with 1,4 BDO | 300 % |
| Full Cure | 3-7 Days |
| Gel Time | 8 Minutes |
| Hardness - ASTM D2240 - A-cured with 1,4 BDO | 88-92 Shore A |
| Initial Cure Time | 1 Hours |
| Open Time - ISO | 8.65-9.05 % |
| POL | 1,4 BDO |
| Post Cure Time | 14-16 Hours |
| Pot Life - 100g | 6 Minutes |
| Resilience, Bayshore % | 58 % |
| Stoichiometry | 95 % |
| Taber Abrasion Resistance - ASTM D4060 - 1000rev, CS 17 | 0.4 mg |
| Tear Strength - ASTM D624, Die C - Cured with 1,4 BDO | 333 pli |
| Tensile Modulus - ASTM D412 - 100%, Cured with 1,4 BDO | 1300 psi |
| Tensile Modulus - ASTM D412 - 200%, Cured with 1,4 BDO | 2100 psi |
| Tensile Modulus - ASTM D412 - 300%, Cured with 1,4 BDO | 3200 psi |
| Tensile Modulus - ASTM D412 - Cured with 1,4 BDO | 3100 psi |
| Tensile Strength - ASTM D412 - Cured with 1,4 BDO | 3100 psi |
| Trouser Tear - ASTM D624, Die T | 12 pli |