Por-A-Thane E-70DTSR is a polyether-based TDI terminated prepolymer which yields a 70-75 Shore D hardness and low viscosity when cured with 4;4’-methylenebis-(orthochloroaniline) commonly known as MOCA.
Advantages
- Excellent humidity resistance
- Good impact strength
- Good Machinability
- High heat distortion temperature
- Low coefficient of friction
- Very high modulus and tensile strength
Product Types
Prepolymer
Product Testing
Test Performed | Test Results |
% NCO - ISO | 9.35-9.65 % |
Elongation - ASTM D412 - Cured with Ethacure 300 | 107 % |
Elongation - ASTM D412 - cured with MOCA | 125 % |
Hardness - ASTM D2240 - Shore D | 70-75 Shore D |
POL | MOCA |
Pot Life - 100g | 1-2 Minutes |
Pot Life - Cured with Ethacure 300 | 2 Minutes |
Ratio by Weight - ISO:POL | 100:28.4 |
Stoichiometry | 95 % |
Tear Strength - ASTM D624 - Cured with Ethacure 300 | 1008 pli |
Tear Strength - ASTM D624 - MOCA cure | 1038 pli |
Tensile Modulus - ASTM D412 - 100%- Ethacure 300 cure | 4532 psi |
Tensile Modulus - ASTM D412 - 100%- MOCA cure | 5323 psi |
Tensile Strength - ASTM D412 - Cured with Ethacure 300 | 5617 psi |
Tensile Strength - ASTM D412 - cured with MOCA | 6460 psi |
Tensile Strength - ASTM D412 - Ethacure 300 cure | 69543 psi |
Tensile Strength - ASTM D412 - MOCA cure | 73589 psi |
Trouser Tear - ASTM D624, Method T - Cured with Ethacure 300 | 298 pli |
Trouser Tear - ASTM D624, Method T - cured with MOCA | 278 pli |