IsoMold URP 5102 is a two-component system that was designed for applications requiring a high level of mechanical properties.
*Physical properties reported were mixed and cured at ambient temperature for 1 hour then post cured at 180F for 16 hours.
Product Types
Elastomer
Product Testing
| Test Performed | Test Results |
| % Solids | 98 |
| Color - ISO | Pale Yellow |
| Color - POL | Yellow |
| Compression Set - Method B, 22 hours @ 158°F | 9.9 % |
| Compressive Strength - ASTM D695 | 642 psi |
| Demold Time | 24 Hours |
| Elongation - ASTM D412 | 203 % |
| Full Cure | 7 Days |
| Gel Time - 100 gram sample, 74°F | 20-30 Minutes |
| Hardness - ASTM D2240 - Shore A | 83 Shore A |
| Initial Cure Temperature | 70-80 °F |
| Initial Cure Time | 1 Hour |
| ISO Processing Temperature | 70-80 °F |
| Mixed Viscosity - ASTM D-2196 - (74°F) | 5400 cps |
| Mold Temperature | 70-80 °F |
| POL Temperature | 70-80 °F |
| Post Cure Temperature | 180 °F |
| Post Cure Time | 16 Hours |
| Pot Life - 100g | 15 Minutes |
| Ratio by Volume - ISO:POL | 2-1 |
| Ratio by Weight - ISO:POL | 100-52 |
| Rebound, Bayshore % - ASTM D2632 | 29 % |
| Shrinkage | 0.55 % |
| Specific Gravity - 74°F, ISO | 1.08 |
| Specific Gravity - 74°F, POL | 1.09 |
| Taber Abrasion Resistance - ASTM D4060 - 1000rev, CS 17 | 10 mg |
| Tear Strength - ASTM D624, Die C | 243 pli |
| Tensile Modulus - ASTM D412 | 3,781 psi |
| Tensile Modulus - ASTM D412 - 100% | 856 psi |
| Tensile Modulus - ASTM D412 - 200% | 1,225 psi |
| Tensile Strength - ASTM D412 | 1,242 psi |
| Trouser Tear - ASTM D624, Die T | 49 pli |
| Viscosity - ASTM D-2196 - 74°F, ISO | 5200-7300 cps |
| Viscosity - ASTM D-2196 - 74°F, POL | 1000-2000 cps |